Microfeature workpiece processing apparatus and methods for controlling deposition of materials on microfeature workpieces

ABSTRACT

The present disclosure provides methods and apparatus useful in depositing materials on batches of microfeature workpieces. One implementation provides a method in which a quantity of a first precursor gas is introduced to an enclosure at a first enclosure pressure. The pressure within the enclosure is reduced to a second enclosure pressure while introducing a purge gas at a first flow rate. The second enclosure pressure may approach or be equal to a steady-state base pressure of the processing system at the first flow rate. After reducing the pressure, the purge gas flow may be increased to a second flow rate and the enclosure pressure may be increased to a third enclosure pressure. Thereafter, a flow of a second precursor gas may be introduced with a pressure within the enclosure at a fourth enclosure pressure; the third enclosure pressure is desirably within about 10 percent of the fourth enclosure pressure.

TECHNICAL FIELD

The present invention is related to equipment and methods for processing microfeature workpieces, e.g., semiconductor wafers. Aspects of the invention have particular utility in connection with batch deposition of materials on microfeature workpieces by atomic layer deposition.

BACKGROUND

Thin film deposition techniques are widely used in the manufacturing of microfeatures to form a coating on a workpiece that closely conforms to the surface topography. In the context of microelectronic components, for example, the size of the individual components in the devices on a wafer is constantly decreasing, and the number of layers in the devices is increasing. As a result, the density of components and the aspect ratios of depressions (e.g., the ratio of the depth to the size of the opening) are increasing. The size of such wafers is also increasing to provide more real estate for forming more dies (i.e., chips) on a single wafer. Many fabricators are currently transitioning from 200 mm to 300 mm workpieces, and even larger workpieces will likely be used in the future. Thin film deposition techniques accordingly strive to produce highly uniform conformal layers that cover the sidewalls, bottoms, and corners in deep depressions that have very small openings.

One widely used thin film deposition technique is chemical vapor deposition (CVD). In a CVD system, one or more precursors that are capable of reacting to form a solid thin film are mixed in a gas or vapor state, and then the precursor mixture is presented to the surface of the workpiece. The surface of the workpiece catalyzes the reaction between the precursors to form a solid thin film at the workpiece surface. A common way to catalyze the reaction at the surface of the workpiece is to heat the workpiece to a temperature that causes the reaction.

Although CVD techniques are useful in many applications, they also have several drawbacks. For example, if the precursors are not highly reactive, then a high workpiece temperature is needed to achieve a reasonable deposition rate. Such high temperatures are not typically desirable because heating the workpiece can be detrimental to the structures and other materials already formed on the workpiece. Implanted or doped materials, for example, can migrate within silicon workpieces at higher temperatures. On the other hand, if more reactive precursors are used so that the workpiece temperature can be lower, then reactions may occur prematurely in the gas phase before reaching the intended surface of the workpiece. This is undesirable because the film quality and uniformity may suffer, and also because it limits the types of precursors that can be used.

Atomic layer deposition (ALD) is another thin film deposition technique. FIGS. 1A and 1B schematically illustrate the basic operation of ALD processes. Referring to FIG. 1A, a layer of gas molecules A coats the surface of a workpiece W. The layer of A molecules is formed by exposing the workpiece W to a precursor gas containing A molecules, and then purging the chamber with a purge gas to remove excess A molecules. This process can form a monolayer of A molecules on the surface of the workpiece W because the A molecules at the surface are held in place during the purge cycle by physical adsorption forces at moderate temperatures or chemisorption forces at higher temperatures. The layer of A molecules is then exposed to another precursor gas containing B molecules. The A molecules react with the B molecules to form an extremely thin layer of solid material C on the workpiece W. The chamber is then purged again with a purge gas to remove excess B molecules.

FIG. 2 illustrates the stages of one cycle for forming a thin solid layer using ALD techniques. A typical cycle includes (a) exposing the workpiece to the first precursor A, (b) purging excess A molecules, (c) exposing the workpiece to the second precursor B, and then (d) purging excess B molecules. The purge process typically comprises introducing a purge gas, which is substantially non-reactive with either precursor, and exhausting the purge gas and excess precursor from the reaction chamber in a pumping step. In actual processing, several cycles are repeated to build a thin film on a workpiece having the desired thickness. For example, each cycle may form a layer having a thickness of approximately 0.5–1.0 Å, and thus it takes approximately 60–120 cycles to form a solid layer having a thickness of approximately 60 Å.

One drawback of ALD processing is that it has a relatively low throughput compared to CVD techniques. For example, ALD processing typically takes several seconds to perform each A-purge-B-purge cycle. This results in a total process time of several minutes to form a single thin layer of only 60 Å. In contrast to ALD processing, CVD techniques only require about one minute to form a 60 Å thick layer. In single-wafer processing chambers, ALD processes can be 500%–2000% longer than corresponding single-wafer CVD processes. The low throughput of existing single-wafer ALD techniques limits the utility of the technology in its current state because ALD may be a bottleneck in the overall manufacturing process.

One promising solution to increase the throughput of ALD processing is processing a plurality of wafers (e.g., 20–250) simultaneously in a batch process. As suggested in International Publication No. WO 02/095807, the entirety of which is incorporated herein by reference, such batch processes typically stack the plurality of wafers in a wafer holder that is positioned in an enclosure of a processing system. To increase the number of wafers that can be treated at one time and concomitantly increase the throughput of the system, the wafers are typically held in a relatively close spaced-apart relationship. Unfortunately, this close spacing between adjacent wafers hinders the flow of gas adjacent the surface of the wafer, particularly adjacent the center of each wafer.

In conventional single-wafer ALD systems, a gas “showerhead” will be spaced in relatively close, parallel proximity with substantially the entirety of the wafer surface. This facilitates thorough, effective purging of the excess precursors A and B. In a batch ALD system, however, gas is typically introduced to flow longitudinally alongside the wafer holder. As a consequence, gas exchange between the wafers takes place, in large part, by gas diffusion rather than a significant flow rate of gas across the wafer surface. To enhance the removal of excess precursor between the wafers, conventional batch ALD processing typically involves introducing a significant quantity of a purge gas to dilute the remaining precursor, then drawing a vacuum on the enclosure to remove the diluted gas. Unfortunately, this addition of excess purge gas and subsequent pump-down can take a relatively long period of time, further reducing the throughput of the batch ALD processing system.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A and 1B are schematic cross-sectional views of stages in ALD processing in accordance with the prior art.

FIG. 2 is a graph illustrating a cycle for forming a layer using ALD techniques in accordance with the prior art.

FIG. 3 is a schematic cross-sectional view of a microfeature workpiece processing system in accordance with an embodiment of the invention.

FIG. 4 is a schematic flow diagram illustrating aspects of a method in accordance with one embodiment of the invention.

FIG. 5 is a flow diagram schematically illustrating aspects of one embodiment of the pump/purge steps in FIG. 4.

FIG. 6 is a graph schematically illustrating gas pressures and flow rates in accordance with one particular embodiment of the invention.

FIG. 7 is a graph schematically illustrating partial pressure of a precursor gas during various pump and/or purge processes.

DETAILED DESCRIPTION

A. Overview

Various embodiments of the present invention provide microfeature workpiece holders, systems including processing chambers, and methods for depositing materials onto microfeature workpieces. Many specific details of the invention are described below with reference to reactors for depositing materials onto microfeature workpieces. The term “microfeature workpiece” is used throughout to include substrates upon which and/or in which microelectronic devices, micromechanical devices, data storage elements, read/write components, and other devices are fabricated. For example, microfeature workpieces can be semiconductor wafers such as silicon or gallium arsenide wafers, glass substrates, insulative substrates, and many other types of materials. The microfeature workpieces typically have submicron features with dimensions of 0.05 microns or greater. Furthermore, the term “gas” is used throughout to include any form of matter that has no fixed shape and will conform in volume to the space available, which specifically includes vapors (i.e., a gas having a temperature less than the critical temperature so that it may be liquefied or solidified by compression at a constant temperature). Several embodiments in accordance with the invention are set forth in FIGS. 3–6 and the following text to provide a thorough understanding of particular embodiments of the invention. A person skilled in the art will understand, however, that the invention may have additional embodiments, or that the invention may be practiced without several of the details of the embodiments shown in FIGS. 3–6.

One embodiment of the invention provides a method of depositing a material on a microfeature workpiece. In accordance with this method, a plurality of microfeature workpieces are positioned in a spaced relationship within an enclosure. A flow of a first precursor gas is introduced to the enclosure at a first enclosure pressure. The flow of the first precursor is terminated and pressure within the enclosure is reduced to a second enclosure pressure while introducing a flow of a purge gas at a first flow rate. The processing system has a base pressure at the first flow rate. A difference between the second enclosure pressure and the first enclosure pressure is at least 90 percent of the difference between the base pressure and the first enclosure pressure. After reducing the pressure within the enclosure to the second enclosure pressure, the flow rate of the purge gas is increased to a second flow rate and the pressure within the enclosure is increased to a third enclosure pressure. After increasing the pressure within the enclosure to the third enclosure pressure, a flow of a second precursor gas is introduced to the enclosure at a fourth enclosure pressure. The third and fourth enclosure pressures may be substantially the same, with any difference between the third and fourth enclosure pressures being about 0–10 percent of the fourth enclosure pressure.

A method in accordance with another embodiment of the invention may also be used to deposit a material on a microfeature workpiece. In this method, a plurality of microfeature workpieces, each of which has a surface, is positioned within an enclosure. The surfaces of the microfeature workpieces are exposed to a first precursor gas at a first enclosure pressure to allow at least a monolayer of the first precursor gas to be adsorbed on the surfaces of the microfeature workpieces. Pressure within the enclosure is reduced to a second, lower enclosure pressure via a pump-down process. The pump-down process comprises withdrawing gas from the enclosure, e.g., with a vacuum, while introducing a purge gas at a first flow rate of no greater than about 250 sccm for a first period of time. This pump-down process reduces the partial pressure of the first precursor gas within the enclosure. After the pump-down process, the enclosure is purged in a purge process that includes introducing the purge gas at a second flow rate of at least about 1000 sccm for a second period of time and allowing the enclosure pressure to increase to a third enclosure pressure that is greater than the second enclosure pressure. After the purge process, the surfaces of the microfeature workpieces may be exposed to a second precursor gas at a fourth enclosure pressure. The third and fourth enclosure pressures may be substantially the same, with any difference between the third and fourth enclosure pressures desirably being about 0–10 percent of the fourth enclosure pressure.

Another embodiment of the invention provides a microfeature workpiece processing system that includes an enclosure, a gas supply, a vacuum, and a programmable controller. The enclosure is adapted to receive a plurality of microfeature workpieces for simultaneous treatment. The gas supply is adapted to selectively deliver a first gaseous precursor, a second gaseous precursor, and a purge gas to the enclosure. The programmable controller is operatively coupled to the gas supply and the vacuum, and the controller may be programmed to carry out one of the aforementioned methods or methods in accordance with other aspects of the invention.

For ease of understanding, the following discussion is subdivided into two areas of emphasis. The first section discusses microfeature workpiece processing systems in accordance with selected embodiments of the invention. The second section outlines methods in accordance with other aspects of the invention.

B. Microfeature Workpiece Processing Systems

FIG. 3 schematically illustrates a reactor 10 in accordance with one embodiment of the invention. This reactor 10 includes a processing enclosure 20 coupled to a gas supply 30 and a vacuum 40. The processing enclosure 20 generally includes an outer wall 22 and an annular liner 24. A platform 60 seals against the outer wall or some other part of the processing enclosure 20 to define a deposition chamber 25. The liner 24 functionally divides the deposition chamber 25 into a main chamber 28 and an annular exhaust 26.

One or more microfeature workpieces W, e.g., semiconductor wafers, may be positioned in the deposition chamber 25 for processing. In the illustrated embodiment, a plurality of microfeature workpieces W are held in the processing enclosure 20 in a workpiece holder 70. It should be understood that FIG. 3 is merely schematic in nature and any number (e.g., 20–250) of workpieces W may be held in the workpiece holder 70 for simultaneous batch processing.

The reactor 10 also includes at least one heat source to heat the workpieces W and maintain them at the desired temperature. The heat source in FIG. 3 is typified as a radiant heater 50 comprising a series of radiant heat panels 50 a and 50 b arranged about a circumference of the enclosure 20 to evenly heat the workpieces W. In one embodiment, these heat panels 50 a–b comprise quartz-halogen lamps or other types of radiative heat sources. In other embodiments, other types of heat sources may be employed. The heater 50 may also include a power supply 52 that is coupled to the first heat panel 50 a by a first power line 54 a and to the second heat panel 50 b by a second power line 54 b.

Gas is introduced from the gas supply 30 to the deposition chamber 25 by a gas line 32 and an inlet 36. The inlet 36 directs a flow of gas into the main chamber 28 of the deposition chamber 25. Under influence of the vacuum 40, gas introduced via the gas inlet 36 will flow through the main chamber 28, outwardly into the annular exhaust 26, and out of the deposition chamber 25. A valve assembly 34 in the gas line 32 may be operated by a controller 90 to selectively deliver gases to the deposition chamber 25 during the deposition phase. In one embodiment, the controller 90 comprises a computer having a programmable processor programmed to control operation of the reactor 10 to deposit material on the workpieces W in accordance with one or more of the methods outlined below. The controller 90 may be coupled to the vacuum 40 to control its operation. The controller 90 may also be operatively connected to the heater 50, e.g., via the power supply 52, to control the temperature of the workpieces W.

Some aspects of the gas supply 30 will depend on the nature of the deposition process to be carried out in the reactor 10. In one embodiment, the reactor 10 is adapted to carry out an ALD process employing multiple precursors. The gas supply 30 in such embodiments can include a plurality of separate gas sources 31 a–c, and the valve assembly 34 may have a plurality of valves. For example, the gas supply 30 may include one or more gaseous precursors capable of reacting to deposit titanium nitride. In one such implementation, the first gas source 31 a is adapted to deliver TiCl₄, the second gas source 31 b is adapted to deliver NH₃, and the third gas source 31 c is adapted to deliver a flow of a purge gas, e.g., nitrogen.

C. Methods of Depositing Materials On Microfeature Workpieces

As noted above, other embodiments of the invention provide methods of processing microfeature workpieces. In the following discussion, reference is made to the particular microfeature workpiece processing system 10 shown in FIG. 3. It should be understood, though, that reference to this particular processing system is solely for purposes of illustration and that the methods outlined below are not limited to any particular processing system shown in the drawings or discussed in detail above.

FIGS. 4 and 5 schematically illustrate aspects of a method of depositing a material on surfaces of a batch of microfeature workpieces in accordance with one embodiment of the invention; FIG. 4 provides an overview, whereas FIG. 5 provides details of certain aspects of FIG. 4. Turning first to FIG. 4, the workpiece manufacturing process 100 may be initiated by positioning the workpieces W in the enclosure 20 of an ALD reactor 10 or other processing system (process 105). In process 110, the ambient atmosphere that entered the main chamber 25 of the enclosure 20 may be withdrawn, e.g., by means of the vacuum 40 and a flow of an inert purge gas (e.g., nitrogen from the third gas source 31 c of the gas supply 30). If necessary, the workpieces W may also be heated to the desired process temperature by the heaters 50.

With the majority of any deleterious gases removed from the deposition chamber 25, a flow of the first precursor gas may be initiated in process 115 and terminated in process 120. This will deliver a pulse of the first precursor gas into the deposition chamber 25, exposing a surface of each of the workpieces W in the deposition chamber 25 to the first precursor. The first precursor may be at least chemisorbed on the workpiece W. Theoretically, such chemisorption will form a monolayer that is uniformly one molecule thick on the entire surface of the workpiece W. Such a monolayer may be referred to as a saturated monolayer. As a practical matter, in some circumstances some minor portions of the workpiece surface may not chemisorb a molecule of the precursor. Nevertheless, such imperfect monolayers are still referred to herein as monolayers. In many applications, a substantially saturated monolayer may be suitable. A substantially saturated monolayer is a monolayer that will yield a deposited layer exhibiting the requisite quality and/or performance parameters.

As is known in the art, an excess of the first precursor gas is typically delivered to the processing enclosure 20. This excess first precursor gas is desirably removed from the vicinity of the workpiece surface prior to introduction of the second precursor gas. Inadequate removal of the first precursor gas prior to introduction of the second precursor gas may result in a gaseous phase reaction between the precursors that yields a material that is less conformal to the topography of the workpiece surface or otherwise adversely affects the quality of the deposited material. Consequently, in the manufacturing process 100 of FIG. 4, a pump/purge process 200 (detailed below) is carried out before introducing the second precursor gas to the enclosure 20. After the pump/purge process 200, a flow of the second precursor gas may be initiated in process 130 to deliver a pulse of the second precursor gas to the enclosure 20. This second precursor may chemisorb on the first monolayer of the first precursor and/or react with the monolayer to form a reaction product. This reaction product is typically one or no more than a few molecules thick, yielding a very thin, highly conformal nanolayer reaction product. After a suitable exposure to the second gaseous precursor, the flow of the second precursor gas may be terminated in process 135 and a pump/purge process 200 may again be performed.

This series of first precursor—pump/purge—second precursor—pump/purge processes may be considered one ALD cycle adapted to deposit a single nanolayer of material. As noted above, the ALD process may need to be repeated a number of times to deposit a layer of material having an appropriate thickness. The manufacturing process 100 of FIG. 4 may thus include a decision process 140 that decides whether the layer deposited on the microfeature workpieces W is thick enough. In many circumstances, this decision will comprise determining whether a fixed number of deposition cycles, which has been empirically determined to deposit an adequate thickness, has been performed. If a sufficient thickness has not been deposited, the manufacturing process 100 may return to process 115 to deposit another thickness of the reaction product. If the thickness is determined in process 140 to be sufficient, though, the workpieces W may be removed from the enclosure 20 in process 145.

FIG. 5 schematically illustrates the pump/purge process 200 of FIG. 4 in greater detail. This pump/purge process 200 generally includes a pump process 210 and a purge process 220. The pump process 210 may include introducing a flow of purge gas at a first flow rate (process 212) and withdrawing gas from the enclosure 20 until a target pressure is reached (process 214). If the vacuum system 40 of the reactor 10 is sufficiently robust, it may be possible to omit the flow of purge gas in process 212 and instead merely withdraw gas from the enclosure 20 with the vacuum 40 in process 214. This will reduce the pressure within the enclosure 20 more rapidly, reducing the time necessary for the pump process 210. For many commercial reactors 10, however, it may be advantageous to continue a flow of purge gas at a relatively low flow rate to reduce the chances of any backflow from or cross-contamination in the vacuum 40.

The first flow rate suitable in process 212 will depend in part on the design of the reactor 10, including its size and geometry, and the precursor being removed. In many commercial applications, though, a first flow rate of no greater than about 250 standard cubic centimeters per minute (sccm) will suffice. A flow rate of 0–250 sccm will be appropriate for most applications, but a flow rate of 50–250 sccm, e.g., 50–100 sccm, is preferred for select embodiments. The particular embodiment illustrated in FIG. 5 shows the introduction of the purge gas in process 212 before withdrawing gas from the enclosure in process 214. In other embodiments, the order of processes 212 and 214 may be reversed or processes 212 and 214 may start and end simultaneously.

After the pump process 210, the pump/purge process 200 of FIG. 5 continues with the purge process 220. This purge process 220 includes increasing the flow of purge gas to a second flow rate in process 222 and increasing pressure in the enclosure 20 to a process pressure 224 that is higher than the target pressure in process 214. In one embodiment, the second flow rate in process 222 is at least about four times the first flow rate (process 212), though this multiple may be significantly higher. It is anticipated that a second flow rate of at least 1000 sccm will be best in most circumstances. In embodiments employing commercial-scale batch ALD reactors 10, a second flow rate of no less than 2000 sccm may be advantageous.

FIGS. 4 and 5 provide an overview of the manufacturing process 100. FIG. 6 provides a schematic illustration of one particular implementation of the manufacturing process 100 that highlights some of the aspects and advantages of select embodiments of the invention. The upper graph of FIG. 6 illustrates the pressure in the processing enclosure 20 over the course of part of the manufacturing process 100. The bottom graph of FIG. 6 is a schematic plot of the flow rate of a purge gas, a first precursor gas, and a second precursor gas as a function of time. The time scale in both graphs of FIG. 6 is the same.

The timeline of FIG. 6 starts with the initiation of the flow of the first precursor gas in process 115 of FIG. 4. (Like reference numbers are used in FIGS. 4–6 to indicate like processes.) The flow of the first precursor gas will continue until it is terminated in process 120, whereupon the pump/purge process 200 may begin. As shown in the top graph of FIG. 6, the pressure in the main chamber 28 of the enclosure 20 may remain substantially constant at a selected process pressure P during the first precursor gas pulse. The process pressure P will vary depending on the nature of the deposition process being carried out, e.g., the nature of the first and second precursor gases, the temperature of the workpieces W, the volume and dimensions of the enclosure 20, and other operating parameters.

As noted above, the pump/purge process 200 includes a pump-down process 210 and a purge process 220. In the pump-down process 210, the flow of purge gas may be relatively low, e.g., 50–100 sccm. With the vacuum 40 activated, the pressure in the main chamber 28 of the enclosure will drop fairly rapidly, as suggested by curve X in the upper graph of FIG. 6. For any particular reactor 10 design and first flow rate during the pump-down process 210, the main chamber 28 of the enclosure 20 will have a substantially steady-state lower pressure identified in FIG. 6 as base pressure B.

In the purge process 220, the flow rate of the purge gas is increased and the pressure within the main chamber 28 of the enclosure 20 is allowed to increase (curve Y). In one particular embodiment, the enclosure pressure at the end of the purge process 220 is similar to the process pressure P at which the workpieces W will be exposed to the second precursor gas. In one particular embodiment, a difference between the enclosure pressure at the end of the purge process 220 and the desired process pressure P at which the workpieces W will be exposed to the second precursor gas is about 0–10% of the process pressure P. In the particular scenario illustrated in the top graph of FIG. 6, the pressure in the enclosure may slightly exceed the process pressure P, but be brought back down to the process pressure P by the end of the pump/purge process 200. If the flow of the second precursor gas were initiated in process 130 when the enclosure pressure is at or close to the base pressure B, the controller 90 is likely to overshoot the desired process pressure P before stabilizing the enclosure pressure. Overshooting the process pressure P with the flow of the second precursor can introduce undesirable variations in the exposure of the workpieces W to the second precursor gas from one cycle to the next. By increasing the enclosure pressure during the purge process 220, the likelihood of overshooting the process pressure P with the second precursor gas can be materially reduced. In the particular scenario illustrated in FIG. 6, the enclosure pressure may overshoot the process pressure P during the purge process 220, but the enclosure pressure may be substantially stabilized at the process pressure P before the flow of the second precursor gas is initiated in process 130. This can enhance uniformity of the process from one cycle to the next.

One objective of the pump/purge process 200 is to reduce the concentration of any excess, nonadsorbed precursor gas in at least the main chamber 28 of the enclosure 20 to an acceptable level. The first precursor—pump/purge—second precursor—pump/purge cycle typically must be repeated numerous times to deposit a suitable thickness of material on the surfaces of the workpieces W. Reducing the time of the pump/purge process 200, therefore, can materially decrease the time needed to reach the suitable material thickness.

FIG. 7 is a schematic graph comparing the expected concentration of a precursor, expressed as a partial pressure of the precursor in the enclosure, during a purge process 220 only, during a pump-down process 210 only, and during a pump/purge process 200 in accordance with embodiments of the invention. In this graph, the process pressure P at which the pump/purge process 200 is initiated is arbitrarily set at 1 (i.e., 0 on the log scale of FIG. 7).

If the pump-down process 210 were omitted and the purge process 220 alone were relied on to reduce concentration of the precursor, one would expect to see the log of the partial pressure of the precursor decrease at a fairly constant rate over time. This is represented in FIG. 7 by dashed curve 320 a, which is generally linear and has a relatively constant first slope S₁. The slope S₁ will vary with a number of factors, including the geometry of the enclosure 20, the relative spacing of the workpieces W, and the rate at which the vacuum withdraws gas from the enclosure. All other factors being equal, though, the slope S₁ generally will increase (i.e., the partial pressure will drop more quickly) with increasing flow rates of purge gas into the enclosure. It should be recognized that curve 320 a is stylized and the partial pressure of the precursor may deviate noticeably from this relatively straight line, particularly at higher purge gas flow rates or higher vacuum extraction rates.

If the purge process 220 were omitted and the pump-down process alone were employed, one would expect to see a marked drop-off in the partial pressure of the precursor in a first phase 310, as illustrated in the solid curve of FIG. 7. Once the base pressure B (FIG. 6) is reached, though, further extraction of precursor from the main chamber 28 of the enclosure 20 is limited largely by the rate at which the precursor diffuses out of the spaces between adjacent workpieces W. Hence, one would expect to see the log of the partial pressure of the precursor decrease at a fairly constant terminal rate during a second phase 312, yielding a generally linear curve having a second slope S₂. This second slope S₂ is expected to be less than the first slope S₁ of curve 320 a. One advantage of the pump-down process 210 is that the partial pressure of the precursor drops off rapidly in the first phase 310 to quickly reduce the partial pressure below a level that promotes further adsorption. This facilitates more precise control over the time the workpieces W are exposed to material concentrations of the precursor.

The pump/purge process 200 illustrated in FIGS. 4–6 is expected to achieve benefits of both the pump-down process 210 and the purge process 220, yet reduce the total time needed to reduce the concentration of precursor in the enclosure to an acceptable level before introducing the next precursor. In the particular example shown in FIG. 7, the pump-down process 210 continues until the enclosure pressure reaches the base pressure B, taking advantage of the rapid decrease in partial pressure of the precursor in the first phase 310 of the pump-down. Rather than continuing the second phase 312 of the pump-down process 210, though, the purge process 220 is initiated promptly after reaching the base pressure B. Curve 320 b, which illustrates the partial pressure of precursor during this purge process 220, may be a relatively straight line having a slope S₃ that is greater than the slope S₂ of the partial pressure curve in the second phase 312 of the pump-down process 210. It is anticipated that the slopes S₁ and S₃ of curves 320 a and 320 b, respectively, will be similar and may be substantially the same. As illustrated in FIG. 7, the increased slope S₃ of curve 320 b compared to slope S₂ during the second pump-down phase 312 will result in a time savings Δt in achieving the same partial pressure of the precursor. As a consequence, the pump/purge process 200 will allow the concentration of precursor in the main chamber 28 of the enclosure 20 to be reduced to the same level in a shorter period of time than either the pump-down process 210 alone (the solid curve in FIG. 7) or the purge process 220 alone (curve 320 a), increasing throughput of the reactor 10.

In the particular embodiment shown in FIG. 7, the purge process 220 is initiated promptly upon reaching the base pressure B. In other embodiments, the pump-down process 210 is allowed to continue for a limited time (e.g., 3 seconds or less) thereafter. Because the slope S₂ of the partial pressure curve in the second phase 312 of the pump-down 210 is less than the slope S₃ of curve 320 b, though, delaying initiation of the purge process 220 will reduce the time savings Δt. In other embodiments, the time purge process 220 is initiated before the base pressure B is reached. In the particular embodiment illustrated in FIG. 6, for example, the purge process 220 starts while the enclosure pressure is slightly higher than the base pressure B achievable in a steady state second phase 312 of the pump-down process 210. In some embodiments of the invention, the purge process 220 is initiated when the difference between the enclosure pressure and the process pressure P is at least 90% of the difference between the base pressure B and the process pressure P. In one particular embodiment, the purge process 220 is initiated when the difference between the enclosure pressure and the process pressure P is at least 90% of the difference between the base pressure B and the process pressure P, but no later than reaching the base pressure. This will achieve the rapid initial drop-off in partial pressure of the precursor, but initiate the purge process 220 before the less productive second phase 312 of the pump-down process 210.

The diffusion rate of any given gas will vary with pressure, with the diffusion rate increasing as pressure is reduced. Different gases diffuse at different rates, though. For example, the diffusion rate D for TiCl₄ in nitrogen is expected to be on the order of 0.032 m²/s at an enclosure pressure of about 1 torr, but this diffusion rate will increase to about 0.80 m²/s at about 0.04 torr. In contrast, NH₃, which may be used as a second precursor with TiCl₄ to deposit TiN, has a diffusion rate D in nitrogen of about 0.088 m²/s at about 1 torr, which climbs to about 2.2 m²/s at about 0.04 torr. NH₃, therefore, should diffuse out of the spaces between the workpieces W more readily than TiCl₄.

The curves 310, 312, 320 a, and 320 b in FIG. 7 are expected to follow the same general relationship for most precursor gases, but the precise shapes of the curves (e.g., the slopes S₁₋₃) will vary from one gas to another. If the pump-down process 210 continues for a fixed time in all pump/purge processes 200 in the manufacturing process 100 of FIG. 4, this time may be selected so the enclosure pressure is reduced by at least 90% of the difference between the base pressure B and the process pressure P for both precursor gases. This may dictate that the enclosure pressure at the end of the pump-down process 210 will vary from one pump/purge process 200 to the next. In another embodiment, the parameters of the pump/purge process 200 may be varied depending on the diffusion characteristics of the precursor gas being purged. This will allow each pump/purge process 200 to be optimized, further enhancing throughput of the reactor 10 without compromising product quality.

The above-detailed embodiments of the invention are not intended to be exhaustive or to limit the invention to the precise form disclosed above. Specific embodiments of, and examples for, the invention are described above for illustrative purposes, but those skilled in the relevant art will recognize that various equivalent modifications are possible within the scope of the invention. For example, whereas steps are presented in a given order, alternative embodiments may perform steps in a different order. The various embodiments described herein can be combined to provide further embodiments.

Unless the context clearly requires otherwise, throughout the description and the claims, the words “comprise,” “comprising,” and the like are to be construed in an inclusive sense as opposed to an exclusive or exhaustive sense, i.e., in a sense of “including, but not limited to.” Use of the word “or” in the claims in reference to a list of items is intended to cover a) any of the items in the list, b) all of the items in the list, and c) any combination of the items in the list.

In general, the terms used in the following claims should not be construed to limit the invention to the specific embodiments disclosed in the specification unless the above-detailed description explicitly defines such terms. While certain aspects of the invention are presented below in certain claim forms, the inventors contemplate various aspects of the invention in any number of claim forms. Accordingly, the inventors reserve the right to add additional claims after filing the application to pursue such additional claim forms for other aspects of the invention. 

1. A method of depositing a material on a plurality of microfeature workpieces held in a spaced relationship within an enclosure of a processing system, the enclosure including a first precursor gas and having a first enclosure pressure, the method comprising: reducing pressure within the enclosure to a second enclosure pressure while introducing a flow of a purge gas into the enclosure at a first flow rate, the second enclosure pressure being less than the first enclosure pressure, the processing system having a base pressure at the first flow rate, and a difference between the second enclosure pressure and the first enclosure pressure being at least 90% of the difference between the base pressure and the first enclosure pressure; and after reducing the pressure within the enclosure to the second enclosure pressure, increasing flow rate of the purge gas to a second flow rate and increasing the pressure within the enclosure to a third enclosure pressure, the second flow rate being greater than the first flow rate and the third enclosure pressure being greater than the second enclosure pressure.
 2. The method of claim 1 wherein the first flow rate is no greater than about 250 sccm.
 3. The method of claim 1 wherein the first flow rate is between about 50 sccm and about 250 sccm.
 4. The method of claim 1 wherein the second flow rate is at least about 1000 sccm.
 5. The method of claim 1 wherein the second flow rate is at least about four times the first flow rate.
 6. The method of claim 1 wherein the third enclosure pressure is at least about nine times the second enclosure pressure.
 7. The method of claim 1 wherein the flow rate of the purge gas is increased to the second flow rate promptly upon reaching the second enclosure pressure.
 8. The method of claim 1 further comprising, after increasing the pressure within the enclosure to the third enclosure pressure, introducing a flow of a second precursor gas to the enclosure with the pressure within the enclosure at a fourth enclosure pressure, a difference between the third enclosure pressure and the fourth enclosure pressure being about 0–10% of the fourth enclosure pressure.
 9. The method of claim 8 wherein the fourth enclosure pressure is approximately equal to the first enclosure pressure.
 10. The method of claim 8 wherein the third enclosure pressure is approximately equal to the fourth enclosure pressure.
 11. The method of claim 8 further comprising, after introducing the flow of the second precursor gas: terminating the flow of the second precursor gas; reducing pressure within the enclosure to the second enclosure pressure while introducing a flow of a purge gas into the enclosure at the first flow rate; and increasing flow rate of the purge gas to the second flow rate and increasing the pressure within the enclosure to the third enclosure pressure.
 12. The method of claim 8 further comprising, after introducing the flow of the second precursor gas: terminating the flow of the second precursor gas; reducing pressure within the enclosure to a fifth enclosure pressure while introducing a flow of a purge gas into the enclosure at the first flow rate, a difference between the fifth enclosure pressure and the first enclosure pressure being at least 90% of the difference between the base pressure and the first enclosure pressure and the fifth enclosure pressure being different from the second enclosure pressure; and increasing flow rate of the purge gas to the second flow rate and increasing the pressure within the enclosure to a sixth enclosure pressure, a difference between the sixth enclosure pressure and the fourth enclosure pressure being about 0–10% of the fourth enclosure pressure.
 13. A method of depositing a material on a microfeature workpiece, comprising: positioning a plurality of microfeature workpieces within an enclosure of a processing system, each of the microfeature workpieces having a surface; exposing the surfaces of the microfeature workpieces to a first precursor gas at a first enclosure pressure to allow at least a monolayer of the first precursor gas to be adsorbed on the surfaces of the microfeature workpieces; reducing pressure within the enclosure to a second, lower enclosure pressure in a pump-down process, the pump-down process comprising withdrawing gas from the enclosure while introducing a purge gas at a first flow rate of no greater than about 250 sccm for a first period of time, the pump-down process reducing a partial pressure of the first precursor gas within the enclosure; and after the pump-down process, purging the enclosure in a purge process, the purge process comprising introducing the purge gas at a second flow rate of at least about 1000 sccm for a second period of time and allowing the enclosure pressure to increase to a third enclosure pressure that is greater than the second enclosure pressure; wherein the processing system has a base pressure at the first flow rate and a difference between the second enclosure pressure and the first enclosure pressure being at least 90% of the difference between the base pressure and the first enclosure pressure.
 14. The method of claim 13 wherein the partial pressure of the first precursor gas within the enclosure decreases at a first rate profile during the pump-down process and the partial pressure of the first precursor gas decreases at a second rate profile during the purge process, the first rate profile having an initial rate and a terminal rate, the initial rate being substantially greater than the second rate and the second rate being greater than the terminal rate.
 15. The method of claim 13 wherein the partial pressure of the first precursor gas within the enclosure is decreased at least two orders of magnitude during the pump-down process.
 16. The method of claim 13 further comprising, after the purge process, exposing the surfaces of the microfeature workpieces to a second precursor gas at a fourth enclosure pressure, a difference between the third enclosure pressure and the fourth enclosure pressure being about 0–10% of the fourth enclosure pressure.
 17. The method of claim 16 wherein the fourth enclosure pressure is approximately equal to the first enclosure pressure.
 18. The method of claim 16 wherein the third enclosure pressure is approximately equal to the fourth enclosure pressure.
 19. The method of claim 16 further comprising, after exposing the surfaces of the microfeature workpieces to the second precursor gas, repeating the pump-down process to reduce a partial pressure of the second precursor gas within the enclosure, then repeating the purge process.
 20. The method of claim 16 wherein the pump-down process is a first pump-down process and the purge process is a first purge process, further comprising, after exposing the surfaces of the microfeature workpieces to the second precursor gas, carrying out a second pump-down process to reduce a partial pressure of the second precursor gas within the enclosure then carrying out a second purge process, the second pump-down process continuing for a third period of time that differs from the first period of time.
 21. A method of depositing titanium nitride on a microfeature workpiece, comprising: positioning a plurality of microfeature workpieces in a spaced relationship within an enclosure of a processing system, each of the microfeature workpieces having a surface; introducing a flow of a first precursor gas to the enclosure to expose the surfaces of the microfeature workpieces to the first precursor gas at a first enclosure pressure and allowing at least a monolayer of the first precursor gas to be adsorbed on the surfaces of the microfeature workpieces, the first precursor gas comprising titanium; reducing pressure within the enclosure by withdrawing gas from the enclosure with a vacuum while introducing a purge gas at a first flow rate of no greater than about 250 sccm for a first period of time to reduce the pressure within the enclosure to a second, lower enclosure pressure and to decrease a partial pressure of the first precursor gas within the enclosure, the processing system having a base pressure at the first flow rate and a difference between the second enclosure pressure and the first enclosure pressure being at least 90% of the difference between the base pressure and the first enclosure pressure; upon reaching the second enclosure pressure, purging the enclosure by withdrawing gas from the enclosure with a vacuum while introducing the purge gas at a second flow rate of at least 1000 sccm for a second period of time and allowing the enclosure pressure to increase to a third enclosure pressure that is greater than the second enclosure pressure and to further decrease the partial pressure of the first precursor gas within the enclosure; and after reaching the third enclosure pressure, exposing the surfaces of the microfeature workpieces to a second precursor gas at a fourth enclosure pressure, a difference between the third enclosure pressure and the fourth enclosure pressure being about 0–10% of the fourth enclosure pressure, the second precursor gas comprising nitrogen.
 22. The method of claim 21 further comprising, after exposing the surfaces of the microfeature workpieces to the second precursor gas: reducing pressure within the enclosure by withdrawing gas from the enclosure with the vacuum while introducing the purge gas at a third flow rate of no greater than about 250 sccm for a third period of time to reduce the pressure within the enclosure to a fifth enclosure pressure and to decrease a partial pressure of the second precursor gas within the enclosure, the processing system having a second base pressure at the third flow rate and a difference between the fifth enclosure pressure and the fourth enclosure pressure being at least 90% of the difference between the second base pressure and the fourth enclosure pressure; and upon reaching the fifth enclosure pressure, purging the enclosure by withdrawing gas from the enclosure with a vacuum while introducing the purge gas at a fourth flow rate of at least 1000 sccm for a second period of time and allowing the enclosure pressure to increase to a sixth enclosure pressure that is greater than the fifth enclosure pressure and to further decrease the partial pressure of the second precursor gas within the enclosure.
 23. A method of depositing a material on a plurality of microfeature workpieces held in a spaced relationship within an enclosure of a processing system, the enclosure including a first precursor gas and having a first enclosure pressure, the method comprising: reducing pressure within the enclosure to a second enclosure pressure that is less than the first enclosure pressure, the processing system having a base pressure and a difference between the second enclosure pressure and the first enclosure pressure being at least 90% of the difference between the base pressure and the first enclosure pressure; after reducing the pressure within the enclosure to the second enclosure pressure, introducing a flow of a purge gas into the enclosure and increasing the pressure within the enclosure to a third enclosure pressure, the third enclosure pressure being greater than the second enclosure pressure; and after increasing the pressure within the enclosure to the third enclosure pressure, introducing a flow of a second precursor gas to the enclosure with the pressure within the enclosure at a fourth enclosure pressure, a difference between the third enclosure pressure and the fourth enclosure pressure being about 0–10% of the fourth enclosure pressure.
 24. The method of claim 23 wherein the fourth enclosure pressure is approximately equal to the first enclosure pressure.
 25. The method of claim 23 wherein the third enclosure pressure is approximately equal to the fourth enclosure pressure.
 26. The method of claim 23 further comprising, after introducing the flow of the second precursor gas: terminating the flow of the second precursor gas; then reducing pressure within the enclosure to the second enclosure pressure; and then introducing a flow of the purge gas and increasing the pressure within the enclosure to the third enclosure pressure.
 27. The method of claim 23 further comprising, after introducing the flow of the second precursor gas: terminating the flow of the second precursor gas; reducing pressure within the enclosure to a fifth enclosure pressure while introducing a flow of the purge gas, a difference between the fifth enclosure pressure and the first enclosure pressure being at least 90% of the difference between the base pressure and the first enclosure pressure and the fifth enclosure pressure being different from the second enclosure pressure; and introducing the purge gas to the enclosure and increasing the pressure within the enclosure to a sixth enclosure pressure, a difference between the sixth enclosure pressure and the fourth enclosure pressure being about 0–10% of the fourth enclosure pressure.
 28. The method of claim 13 wherein the first flow rate is at least about 50 sccm.
 29. The method of claim 13 wherein the second flow rate is at least about 2000 sccm.
 30. The method of claim 13 wherein the third enclosure pressure is at least about nine times the second enclosure pressure.
 31. The method of claim 13 wherein the flow rate of the purge gas is increased to the second flow rate promptly upon reaching the second enclosure pressure. 